Technical Specifications

DIN 127B / GB/T 93 / ASME B18.21.1 Spring Lock Washers Hardness:420 - 510 HV (Carbon Steel); HV ≥ 200 (Stainless Steel)140 HV / 200 HV / 300 H	 Plain, Zinc Plated, Hot Dip Galvanized, Mechanical Galv
Collapse Images
DIN 127B / GB/T 93 / ASME B18.21.1 Spring Lock Washers Hardness:420 - 510 HV (Carbon Steel); HV ≥ 200 (Stainless Steel)140 HV / 200 HV / 300 H	 Plain, Zinc Plated, Hot Dip Galvanized, Mechanical Galv
DIN 127B / GB/T 93 / ASME B18.21.1 Spring Lock Washers Hardness:420 - 510 HV (Carbon Steel); HV ≥ 200 (Stainless Steel)140 HV / 200 HV / 300 H	 Plain, Zinc Plated, Hot Dip Galvanized, Mechanical Galv
DIN 127B / GB/T 93 / ASME B18.21.1 Spring Lock Washers Hardness:420 - 510 HV (Carbon Steel); HV ≥ 200 (Stainless Steel)140 HV / 200 HV / 300 H	 Plain, Zinc Plated, Hot Dip Galvanized, Mechanical Galv

Standard

DIN 127B / GB/T 93 / ASME B18.21.1

Specification

M2 - M100

Material

Spring Steel(65Mn), Stainless Steel (A2/A4)

Property Class

Hardness:420 - 510 HV (Carbon Steel); HV ≥ 200 (Stainless Steel)140 HV / 200 HV / 300 H

Finish

Plain, Zinc Plated, Hot Dip Galvanized, Mechanical Galv

Product Description

Form B: Square ends

Technical Data & Drawings
Model: DIN 127B / GB/T 93 / ASME B18.21.1 Spring Lock Washers pdf
Loading...

Packaging & Delivery

Surface Anti-Rust Treatment

Since spring steel is highly susceptible to oxidation, all products undergo a dewatering anti-rust oil immersion process before dispatch to ensure long-term protection during maritime transit.


Sorting & Inner Packaging

For small to medium sizes (M2–M12), we provide premium EternalFast blue-and-white branded boxes (standard 1,000 pcs/box) for easy inventory management and retail display.


Logistics & Weight Optimization

As spring washers are lightweight components, we recommend shipping them as "filler cargo" alongside heavy hex bolts and nuts. This helps optimize the container's weight-to-volume ratio and significantly reduces overall freight costs per unit.


Quality & Certificates

Elasticity Recovery Test

We perform random sampling for the "Triple Compression Test." Each washer is pressed flat three times; the permanent set is measured to ensure the free height recovery rate is no less than 90% of the original standard.


Hydrogen Embrittlement Mitigation

To prevent catastrophic brittle failure in electro-galvanized (zinc-plated) spring washers, we strictly implement a de-embrittlement baking process (200°C for 8 hours) within 4 hours of the plating completion.

Documentary Support

Every shipment is accompanied by a Material Test Report (MTC) 3.1, detailing the chemical composition (65Mn/AISI 1065) and hardness test results (420–510 HV).